Each of the new Dual Shield II H4 wires is an all-position flux cored wire that provides excellent low temperature toughness in both the as welded and/or stress relieved conditions (as applicable) when used with 75% argon/25% CO2. Each can produce diffusible hydrogen levels of less than 4 mL/100 g over a wide range of welding parameters. Dual Shield II 70T-12H4 also provides the smooth arc and low spatter levels characteristic of other Dual Shield II wires. Dual Shield II 70T-12H4 can be used in construction, heavy equipment fabrication, offshore oil components, shipbuilding, and railcar. Weld metal analysis is similar to E7018
- 24.5 - 29 volt (shielding gas C-25)
- 200 - 500 in./min. wire feed speed (shielding gas C-25)
- 3.8 - 9.9 deposition rate (shielding gas C-25)
- 81.5 - 84.6% efficiency
ESAB Dual Shield II 70T-12H4 245016290 Mild Steel Flux-Cored Wire, Gas Shielded, Diameter: 045 Inch, Amperage: 145 - 285 amp, Package: 33 lb Plastic Spool Vacuum Pack, AWS Class: AWS A5.20: E71T-1MJH4/T-9MJH4/T-12MJH4, Tensile Strength: 80 ksi (As Welded), Yield Strength: 72 ksi (As Welded), Elongation in 2" (%): 27% (As Welded), Charpy V-Notch: 79 ft.-lb. At -29 deg C Testing Temperature (As Welded), Reduction in Area: 71% (As Welded), Welding Process: FCAW (Flux Core), Weld Metal Composition: 0.049% Carbon (C), 1.18% Manganese (Mn), 0.37% Silicon (Si), 0.012% Phosphorus (P), 0.007% Sulphur (S), Melting Range: >1000 deg C