Dual Shield II 70 Ultra is an all-position flux cored wire that displays exceptional impact properties when used with 75% argon/25% CO2. The improved properties qualify this wire to the Navy s "HY" classifi cation. The "Ultra" series produces smoother arc characteristics and lower welding fumes. Dual Shield II 70 Ultra was developed to join low and medium carbon steel. The military classification allows Dual Shield II 70 Ultra to be used for attaching steels of less than 81 ksi (560 MPa) yield to HY-80 and HY-100

• Outstanding all position performance and a fume emission rate approaching that of solid wires
• Very wide operating window, very high out of position deposition rates (vertical up and overhead at over 12 lb/hr), and welds that are virtually spatter free
• 22 - 26 volt
• 200 - 500 in./min. wire feed speed
• 3.94 - 9.52 lb/hr deposition rate
• 82.08 - 87.55% efficiency

ESAB Dual Shield II 70 Ultra 245013313 Mild Steel Flux-Cored Wire, Gas Shielded, Diameter: 045 Inch, Amperage: 145 - 275 amp, Package: 33 lb Plastic Spool, AWS Class: AWS A5.20: E71T-1M/T-9M/T-12M, Tensile Strength: 81 ksi (As Welded), Yield Strength: 72 ksi (As Welded), Elongation in 2" (%): 29% (As Welded), Charpy V-Notch: 70 ft.-lb. At -29 deg C Testing Temperature (As Welded 75% Argon/25% CO2), Reduction in Area: 75% (As Welded), Welding Process: FCAW (Flux Core), Weld Metal Composition: 0.04% Carbon (C), 1.0% Manganese (Mn), 0.4% Silicon (Si), 0.008% Phosphorus (P), 0.009% Sulphur (S), Melting Range: >1000 deg C, Applicable Materials: Low And Medium Carbon Steel