Sandvik Er316l Welding Wire, 3/32 Inch Dia. X 36 Inch L 2B316L093T SAN2B316L093T

Detailed Description

Sandvik 19.12.3.L is a filler material for joining stainless CrNiMo and CrNi steels, stabilized or non-stabilized, e.g. ASTM 316, 316L and 316Ti as well as 304, 304L, 321 and 347, used for service temperatures up to 400 deg C (750 deg F), stainless Cr steels with max 19% Cr. Sandvik 19.12.3.L is available as wire and rods for MIG/MAG, TIG, plasma-arc and submerged-arc welding

Features
  • Sandvik 19.12.3L has good resistance to general corrosion
  • Due to its low carbon content, good resistance to intercrystalline corrosion
  • It also has good resistance to pitting corrosion due to the balanced molybdenum content
  • The parameters for TIG welding depend largely upon the base metal thickness and the welding application
  • Electrode negative and a shielding gas of argon or helium should be used to prevent oxidation of the weld metal
  • 28 - 32 volt (SAW)
  • 160 HV At 20 deg C hardness
  • 15 - 20 W/m at 20 - 500 deg C thermal conductivity

Sandvik 2B316L093T Welding Wire, Diameter: 3/32 Inch, Length: 36 Inch, Amperage: 250 - 400 amp (SAW), AWS Class: AWS SFA5.9: ER316L, Tensile Strength: 610 MPa at 20 deg C, Yield Strength: 410 MPa At 20 deg C, Elongation in 2" (%): 35% At 20 deg C, Charpy V-Notch: 110 J At 20 deg C, Reduction in Area: 40% At 20 deg C, Welding Process: TIG (GTAW)/MIG/MAG/PAW/SAW, Weld Metal Composition: <0.020% Carbon (C), 0.4% Silicon (Si), 1.8% Manganese (Mn), <0.025% Phosphorus (P), <0.015% Sulphur (S), 18.5% Chromium (Cr), 12.5% Nickel (Ni), 2.6% Molybdenum (Mo), <0.060% Nitrogen (N), Applicable Materials: Stainless CrNiMo, CrNi Steel

Technical Details

Amperage
250 - 400 amp (SAW)
Applicable Materials
Stainless CrNiMo, CrNi Steel
AWS Class
AWS SFA5.9: ER316L
Charpy V-Notch
110 J At 20 deg C
Diameter
3/32 Inch
Elongation in 2" (%)
35% At 20 deg C
Length
36 Inch
Reduction in Area
40% At 20 deg C
Tensile Strength
610 MPa at 20 deg C
Weld Metal Composition
<0.020% Carbon (C), 0.4% Silicon (Si), 1.8% Manganese (Mn), <0.025% Phosphorus (P), <0.015% Sulphur (S), 18.5% Chromium (Cr), 12.5% Nickel (Ni), 2.6% Molybdenum (Mo), <0.060% Nitrogen (N)
Welding Process
TIG (GTAW)/MIG/MAG/PAW/SAW
Yield Strength
410 MPa At 20 deg C