Sandvik 24.13.L is suitable for joining stainless Cr-Ni steels of the 309 type, Cr-steels and dissimilar steels e.g. austenitic stainless steel to carbon or low-alloyed steels for service up to 320 deg C (610 deg F). It is used for MIG/MAG-, TIG-, plasma-arc and submerged-arc welding
- Sandvik 24.13.L is normally used for joints between non alloyed or low alloyed steels and stainless steels where resistance to corrosion is of secondary importance
- The parameters for TIG welding depend largely upon the base metal thickness and the welding application
- Electrode negative and a shielding gas of argon or helium should be used to prevent oxidation of the weld metal
- 29 - 34 volt (SAW)
- 160 HV at 20 deg C hardness
- 14 - 18 W/m at 20 - 500 deg C thermal conductivity
Sandvik 2B309L125T Welding Wire, Diameter: 1/8 Inch, Length: 36 Inch, Amperage: 300 - 500 amp (SAW), AWS Class: AWS SFA5.9: ER309L, Tensile Strength: 600 MPa at 20 deg C, Yield Strength: 400 MPa At 20 deg C, Elongation in 2" (%): 40% At 20 deg C, Charpy V-Notch: 140 J At 20 deg C, Reduction in Area: 60% At 20 deg C, Welding Process: TIG (GTAW)/MIG/MAG/PAW/SAW, Weld Metal Composition: <0.02% Carbon (C), 0.4% Silicon (Si), 1.8% Manganese (Mn), <0.02% Phosphorus (P), <0.015% Sulphur (S), 23.5% Chromium (Cr), 13.5% Nickel (Ni), <0.3% Molybdenum (Mo), <0.1% Cobalt (Co), <0.2% Copper (Cu), Applicable Materials: Stainless Cr-Ni Steel Of The 309 Type, Cr-Steels And Dissimilar Steel