Kobelco DW stainless series MIG wire is less voltage sensitive with less spattering and a higher deposition rate. It has good bead appearance and is easier to do multi-pass welding. CO2 gas is recommended so associated gas costs are lower
- Excellent performance in flat and horizontal position with either 75% argon - 25% Co2 gas mixture or 100% Co2
- Easy slag removal greatly reduces the cleaning time after welding
- Due to less spattering and small spatter size, adhesion of spatter to the base metal is almost eliminated
- Flux-cored wire consists of a tube of 18/8-material filled with a granular core of flux
- The flux contains both slag-forming compounds and alloying elements
- The composition of the flux is important for the welding properties obtained as well as the chemical composition and strength of the weld metal
- 24 - 33 volt
- 210 - 610 in./min. wire feed speed
- 5 - 12 lb/hr deposition rate
Kobelco Premiarc DW309L04528 Stainless Steel Flux-Cored Wire, Gas Shielded, Diameter: .045 Inch, Current Type: DC+, Amperage: 130 - 250 amp, Package: 28 lb Spool, AWS Class: AWS A5.22: E309LT0-1, AWS A5.22: E309LT0-4, Tensile Strength: 81218 psi (100% CO2), Yield Strength: 60907 psi 0.2% (100% CO2), Elongation in 2" (%): 34% (100% CO2), Reduction in Area: 0.42, Welding Process: FCAW (Flux Core)/MIG, Weld Metal Composition: 0.03% Carbon (C), 1.24% Manganese (Mn), 0.48% Silicon (Si), 0.016% Phosphorus (P), 0.011% Sulphur (S), 12.49% Nickel (Ni), 23.73% Chromium (Cr), 0.018% Nitrogen (N), 19.2% FN, Applicable Materials: Unalloyed Steel, Stainless To Unalloyed Or Low-Alloy Steel, Certain High-Temperature Steel