Hobart 447A S113844-031 Rutile Potassium E6013 Welding Electrode, 1/8 Inch Dia., 50 Lb Carton S113844-031 HOBS113844-031

Hobart® 447A S113844-031 Rutile Potassium E6013 Welding Electrode, 1/8 Inch dia., 50 lb Carton

$172.95 / 50 lb can
8% off list $188.55
Our Id: HOBS113844-031
Manufacturer Id: S113844-031
Check Store Inventory

Detailed Description

Fast freeze characteristics make this the perfect choice for welding applications that have poor fit-up conditions. Produces a very stable arc with good weld bead appearance. Excellent choice for sheet metal welding

Features
  • Excellent arc stability
  • Welding accuracy and efficiency
  • Fast-freeze
  • Excellent for poor fit-up
  • Welds in flat, horizontal, vertical and overhead positions
  • Slag removes easily
  • Quick clean-up
  • 1.85 lb/hr at 100 amp deposition rate, 66.1% at 100 amp efficiency
  • Physical state: cored wire, form: coated rod, color: gray
  • 18.5 - 22.5 volt

Hobart® Hobart® 447A S113844-031 Welding Electrode, Diameter: 1/8 Inch, Current Type: AC/DC+/-, Amperage: 70 - 120 amp, Package: 50 lb Carton, AWS Class: AWS A5.1: E6013, Coating: Rutile Potassium, Tensile Strength: 74000 psi (As Welded), Yield Strength: 67000 psi (As Welded), Elongation in 2" (%): 30% (As Welded), Reduction in Area: 25 - 55% (As Welded), Welding Process: SMAW (Stick), Weld Metal Composition: 0.08% Carbon (C), 0.39% Manganese (Mn), 0.012% Phosphorus (P), 0.016% Sulfur (S), 0.25% Silicon (Si), 0.04% Nickel (Ni), 0.04% Chromium (Cr), 0.01% Molybdenum (Mo), 0.01% Vanadium (V), Applicable Materials: Mild Steel, Sheet Metal

Technical Details

Amperage
70 - 120 amp
Applicable Materials
Mild Steel, Sheet Metal
AWS Class
AWS A5.1: E6013
Coating
Rutile Potassium
Current Type
AC/DC+/-
Diameter
1/8 Inch
Elongation in 2" (%)
30% (As Welded)
Package
50 lb Carton
Reduction in Area
25 - 55% (As Welded)
Tensile Strength
74000 psi (As Welded)
Weld Metal Composition
0.08% Carbon (C), 0.39% Manganese (Mn), 0.012% Phosphorus (P), 0.016% Sulfur (S), 0.25% Silicon (Si), 0.04% Nickel (Ni), 0.04% Chromium (Cr), 0.01% Molybdenum (Mo), 0.01% Vanadium (V)
Welding Process
SMAW (Stick)
Yield Strength
67000 psi (As Welded)