Washington Alloy low fuming bronze is a general-purpose oxyacetylene brazing rod used for steel, copper alloys, cast iron, nickel alloys and stainless steel. A balanced chemical analysis of copper and zinc as well as alloying elements of tin, iron, manganese and silicon produce weld deposits are easily attained simply by applying a neutral or slightly oxidizing flame. The high silicon content of Washington alloy low fuming bronze keeps fumes to a minimum. Preheating is required for some applications and bronze brazing flux is required for the bare rods
- 1590 deg F solidus temperature
- 1630 deg F liquidus temperature
- 1330 - 1550 deg F brazing range
- 80 - 100 brinell hardness
- Preheating is required for some applications and bronze brazing flux is required for the bare rods
Washington® TCULFB05 Flux Coated Rod, Low Fuming Bronze Alloy, Diameter: 3/32 Inch, AWS Class: AWS A5.8/A5.8M RBCuZn-C, Coating: Yellow Brass, Tensile Strength: 60 - 68000 psi, Weld Metal Composition: 56.0 - 60.0% Copper (Cu), Balance Zinc (Zn), 0.80 - 1.10% Tin (Sn), 0.25 - 1.20% Iron (Fe), 0.01 - 0.50% Manganese (Mn), 0.04 - 0.15% Silicon (Si), Applicable Materials: Steel, Copper Alloys, Cast Iron, Nickel Alloys, Stainless Steel