Unibraze 410 is used to weld stainless grades 403, 405, 410, 416 and for welding overlay on carbon steels to resist corrosion, erosion, or abrasion. Since Unibraze 410 is an air hardening type of material the joint should be preheated to 350 deg F
- 98/99% argon + 2/1% O, 97% argon + 3% Co2 shielding gas for MIG
- 100% argon shielding gas for TIG
- 30 - 50 cfh gas flow
- 26 - 29 volt
Unibraze® 41003530 Welding Wire, Gas Shielded, Diameter: 0.035 Inch, Amperage: 160/210 amp, Package: 30 lb Spool, AWS Class: AWS A5.9, Tensile Strength: 89000 psi (As Welded Post Weld Heat Treatment 1350 - 1400 deg For One Hour), Yield Strength: 78500 psi (As Welded Post Weld Heat Treatment 1350 - 1400 deg For 1 hr), Elongation in 2" (%): 24% (As Welded Post Weld Heat Treatment 1350 - 1400 deg For 1 hr), Welding Process: TIG (GTAW)/MIG/SAW, Weld Metal Composition: 0.12% Carbon (C), 11.5 - 13.5% Chromium (Cr), 0.60% Nickel (Ni), 0.75% Molybdenum (Mo), 0.60% Manganese (Mn), 0.50% Silicon (Si), 0.03% Phosphorus (P), 0.03% Sulphur (S), 0.75% Copper (Cu), Applicable Materials: 403, 405, 410, 416 Stainless Steel, Carbon Steel