Sandvik 24.13.L is suitable for joining stainless CrNi steels of the 309 type, Crsteels and dissimilar steels e.g. austenitic stainless steel to carbon or lowalloyed steels for service up to 320 deg C (610 deg F). It is used for MIG/MAG, TIG, plasmaarc and submergedarc welding
- Electrode positive is used to give good penetration in all types of welded joint
- 160 HV hardness
- 28 32 volt
Sandvik 2B309L09360 Welding Wire, Diameter: 3/32 Inch, Amperage: 250 - 450 amp, Package: 60 lb Coil, AWS Class: AWS A5.9: ER309L, Tensile Strength: 600 MPa, Yield Strength: 400 MPa, Elongation in 2" (%): 40% (As Welded), Charpy V-Notch: 140 J At 20 deg C, Reduction in Area: 60% At 20 deg C, Welding Process: MIG (GMAW And SAW), Weld Metal Composition: <0.02% Carbon (C), 0.4% Silicon (Si), 1.8% Manganese (Mn), <0.02% Phosphorus (P), <0.015% Sulphur (S), 23.5% Chromium (Cr), 13.5% Nickel (Ni), < 0.3% Molybdenum (Mo), < 0.1% Cobalt (Co), < 0.2% Copper (Cu)