Self-shielded, flux-cored wire with higher hardness for metal-to-metal wear and mild abrasion. Used on transfer rollers and guides, crane wheels and shafts

• Delivers a deposit which resists metal-to-metal rolling or sliding wear as well as mild abrasion
• Designed for semiautomatic and automatic welding
• Long stickout is used for maximum efficiency and minimum penetration
• Intended for downhand use and for horizontal stringer beads on sloped surfaces
• Flat, horizontal welding positions
• 24 - 30 volt
• 7.0 - 13.7 lb/hr deposition rate
• 3.2 - 6.4 m/min (wire feed speed)
• 1-2 (no. of layers), 50-59/50-60 (as welded), 53-62/56-62 (work-hardened), 50-55/55-59 (350 deg F interpass temp), 52-54 (flame-hardened/water quenched)

Lincoln® Lincore® 55 ED011278 Hard Facing Flux-Cored Wire, Self-Shielded, Diameter: 5/64 Inch, Current Type: DC+, Amperage: 190 - 330 amp, Package: 50 lb Coil, Welding Process: FCAW, Weld Metal Composition: 0.45% Carbon (C), 1.4% Manganese (Mn), 0.60% Silicon (Si), 1.4% Aluminum (Al), 5.3% Chromium (Cr), 0.80% Molybdenum (Mo), 0.004% Sulfur (S), 0.010% Phosphorus (P), Applicable Materials: Carbon, Low Alloy And Manganese Steel