Bohler Thyssen T-Put 72740 Low Hydrogen Iron Powder E7018-1 Welding Electrode, 3/32 Inch Dia. X 14 Inch L, 8 Lb 72740 BOH72740

Detailed Description

Phoenix 120K is a basic covered electrode. Very good welding characteristics including out of position work; 120% weld meal recovery; H2-content in the weld metal less than 5 mL/100 g; very pure cryogenic weld metal at temperatures as low as -50 deg C (-58 deg F); CTOD tested up to -10 deg C (14 deg F). Suitable for use in structural steel work, boiler making, tank construction, ship and bridge building and vehicle manufacture; particularly suitable for welding fine grained structural steels. Excellent weldability on offshore steels. Redry for 2 hr at 250-350 deg C (482-662 deg F)

Bohler Thyssen T-PUT 72740 Welding Electrode, Diameter: 3/32 Inch, Length: 14 Inch, Current Type: AC/DC+, Amperage: 65 - 110 amp, Package: 8 lb, AWS Class: AWS A5.1: E7018-1, Coating: Low Hydrogen Iron Powder, Tensile Strength: 510 MPa, Yield Strength: 420 MPa, Elongation in 2" (%): 22%, Charpy V-Notch: 47 J At -50 deg C, Welding Process: SMAW (Stick), Weld Metal Composition: 0.07% Carbon (C), 0.35% Silicon (Si), 1.2% Manganese (Mn), Applicable Materials: Structural Steel

Technical Details

Amperage
65 - 110 amp
Applicable Materials
Structural Steel
AWS Class
AWS A5.1: E7018-1
Charpy V-Notch
47 J At -50 deg C
Coating
Low Hydrogen Iron Powder
Current Type
AC/DC+
Diameter
3/32 Inch
Elongation in 2" (%)
22%
Length
14 Inch
Package
8 lb
Tensile Strength
510 MPa
Weld Metal Composition
0.07% Carbon (C), 0.35% Silicon (Si), 1.2% Manganese (Mn)
Welding Process
SMAW (Stick)
Yield Strength
420 MPa